Snapmaker SnapSpeed PLA Filament (1kg, RFID)- Cool White 2 Pack

Snapmaker SnapSpeed PLA Filament (1kg, RFID)

Snapmaker SnapSpeed PLA is engineered for high-speed printing through an optimised formula based on regular PLA. Featuring enhanced melt fluidity, it significantly boosts printing speed while maintaining accuracy and surface quality. It is ideal for model creation and prototyping, with wide applications in toys and games, creative home decor, hobbies and DIY, as well as fashion and arts.

Key Features:

-            High-speed printing up to 300 mm/s with stable, consistent output.

-            Strong layer adhesion creates clean, solid prints—even at high speed.

-            RFID recognition automatically loads preset filament information on Snapmaker U1.

-            Easy to print and widely compatible with FDM 3D printers.

Specification:

RECOMMENDED PRINTING CONDITIONS5

*Based on a 0.4mm nozzle. Printing conditions may vary with different nozzle diameters.

Nozzle temperature: Classic: 190–210 °C; High-speed: 210–230 °C

Build plate temperature: 25–60 °C

Build surface treatment: Glue when needed

Printing speed: Classic: 50-100mm/s; High-speed: 100-300mm/s

Drying setting: 55°C for 6h

PHYSICAL PROPERTIES

Density: 1.23g/cm³ at 21.5°C

Melt index: 15.4 g/10min

THERMAL PROPERTIES

Glass transition temperature: 59°C

Melting temperature: 164°C

Crystallization temperature: 96°C

Decomposition temperature: 370°C

Vicat softening temperature: 61°C

Heat deflection temperature (ISO 75 1.8MPa): 52°C

Heat deflection temperature (ISO 75 0.45MPa): 53°C

MECHANICAL PROPERTIES - Classic Speed

*Based on 0.4mm nozzle and 0.2mm layer thickness. Classic prirhting speed = 46.7mm/s, printing temperature = 210 °C

Young's modulus (X-Y): 2878.3±74.3 MPa

Young's modulus (Z): 2689.8±92.0 MPa

Tensile strength (X-Y): 46.0±0.5 MPa

Tensile strength (Z): 37.3±0.7 MPa

Elongation at break: 21.5±5.02%

Elongation at break (Z): 4.2±2.0%

Bending modulus (X-Y): 2868.2±78.4 MPa

Bending strength (X-Y): 76.5±0.9 MPa

Charpy impact strength (X-Y): 6.1±0.6 kJ/m²

MECHANICAL PROPERTIES - High Speed

*Based on 0.4mm nozzle and 0.2mm layer thickness. High printing speed = 300mm/s, printing temperature = 230 °C

Young's modulus (X-Y): 2649.7±78.3 MPa

Young's modulus (Z): 2433.4±79.4 MPa

Tensile strength (X-Y): 43.9±0.4 MPa

Tensile strength (Z): 32.4±0.4 MPa

Elongation at break: 15.1±3.9%

Elongation at break (Z): 3.3±0.5%

Bending modulus (X-Y): 2797.9±40.7 MPa

Bending strength (X-Y): 71.4±0.6 MPa

Charpy impact strength (X-Y): 5.0±0.5 kJ/m²

Dimension:
Product Dimension: 200*190*60mm

Package Dimension: 220*210*70mm

What is in the box:

1Kg Spool of filament x 2